The choice for an ASTM B705 UNS N06625 Welded Pipe persists despite the fact that seamless pipes typically have an operational working pressure 20% higher than that of welded pipes. This is partly because they are a more affordable option. A big sheet with a longitudinal weld seam is first welded in the production of an ASTM B705 Inconel Incoloy Alloy Welded Pipe. The welding procedure is automatic, and the sheet is essentially a flat-rolled alloy.
The cold worked, ASME SB705 nickel alloy welded pipe is delivered in an annealed state. After using the cold working technique, ASME SB 705 N08825 Pipes must undergo an annealing treatment to restore the material's ductility. As a result, it is known that annealing enables further processing of the metal without the ASTM B705 Welded Pipe (625/825) cracking. This is due to the release of extra mechanical stresses during annealing. Operations like grinding and machining place mechanical strains on the ASTM B705 Tubing material.
Thus, applying an annealing treatment to astm b705 class 1 welded pipe simply helps to minimise deformation that may be brought on by using higher temperatures for the future heat treatment processes. Many manufacturers also conduct a non-destructive test on the welded ASTM B705 Inconel Pipe in addition to cold working and annealing. The ASTM B705 Welded Pipe is susceptible to nondestructive tests such as hydrostatic testing, pneumatic testing, eddy current testing, ultrasonic testing, leak testing, and electrical testing.
| Standard | ASTM, ASME, JIS, AISI, AMS, EN, SAE, DIN, NF, TOCT, DS, DTD, GB |
|---|---|
| Size | 4 to 219mm W. T.: 0.5 to 20mm |
| Swg & Bwg | 10 Swg., 12 Swg., 14 Swg., 16 Swg., 18 Swg., 20 Swg. |
| Schedule | SCH5, SCH10, SCH10S, SCH20, SCH30, SCH40, SCH40S, STD, SCH80, XS, SCH60, SCH80, SCH120, SCH140, SCH160, XXS |
| Length | Single Random, Double Random, Standard & Cut length Pipe |
| Finish | Polished, AP (Annealed & Pickled), BA (Bright & Annealed), MF, NO.1, NO.4, 2B, BA, HL, 8K, Mirror finish, etc |
| Form | Round, Square, Hollow, Rectangular, Hydraulic, Coiled, Straight Pipes, “U” Shape, Pan Cake Coils etc. |
| Type | Seamless / ERW/ EFW / Welded / Fabricated / CDW / DOM / CEW |
| End | Plain End, Beveled End, Treaded Pipe, Screwed ends |
| Product | Country |
|---|---|
| 3 mm ASTM B705 UNS N06625 Pipe Cladded | Singapore, South Africa, Bahrain |
| 2" ASME SB 705 N08825 pipe, SCH 80 | Russia, Dubai, Malaysia, Netherlands |
| 26.7mm x 5.56mm Sch 160 UNS N06625 | Canada, Singapore, Malaysia, Philippines |
| Grade | C | Mn | Si | Fe | S | Cr2 | Al-Ti | Ni | |
|---|---|---|---|---|---|---|---|---|---|
| 625 | min. | – | – | – | – | – | 20.0 | – | 58.0 |
| max. | 0.10 | 0.50 | 0.50 | 5.0 | 0.015 | 23.0 | 0.40 | – | |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
|---|---|---|---|---|---|
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 625 | Psi – 1,35,000 , MPa -930 | Psi – 75,000 , MPa – 517 | 42.5 | – | – |